高铝支撑剂主要含量以氧化铝为主,具有足够化学稳定性和热稳定性的瓷球。作为反应器内催化剂的支撑、覆盖材料及塔填料,广泛用于化工、化肥、冶炼、天然气、陶瓷等行业。它具有纯度高、强度好、耐磨、耐高温、耐强酸和强碱等特点。
规格:φ3一φ75mm
外观:白色球体
分析标准:化工行业标准GB/T3044-2007 《白刚玉、铬刚玉分析方法》
主要化学成份
成份\Al2O3含量 | 高铝支撑剂 | ||||
90% | 93% | 95% | 97% | 99.5% | |
Al2O3 | ≥90% | ≥93% | ≥95% | ≥97% | ≥995% |
SiO2 | ≤5% | ≤4% | ≤3% | ≤1% | ≤0.2% |
Fe2O3 | ≤0.5% | ≤O.5% | ≤0.1% | ≤0.1% | ≤0.05% |
MgO | ≤1% | ≤1% | ≤1% | ≤0.5% | ≤0.05% |
Na2O+K2O | ≤1% | ≤1% | ≤1% | ≤0.5% | Na2O≤0.2% |
CaO | ≤1% | ≤1% | ≤1% | ≤0.5% | ≤O.02% |
主要技术指标
物理性能\Al2O3 | 高铝支撑剂 | |||||
90% | 93% | 95% | 97% | 99.5% | ||
耐热温度℃ | 1450℃ | 1500℃ | 1550℃ | 1600℃ | 1650℃ | |
吸水率% | ≤4% | |||||
耐酸度% | ≥98% | |||||
耐碱度% | ≥96% | |||||
耐温度急变℃ | ≥800℃ | |||||
抗压强度 KN/颗 |
φ3 | ≥O.20 | ≥0.25 | ≥O.3 | ≥O.4 | ≥0.5 |
φ6 | ≥0.50 | ≥O.60 | ≥O.8 | ≥1.0 | ≥1.2 | |
φ8 | ≥O.65 | ≥0.8 | ≥1.0 | ≥1.2 | ≥1.6 | |
φ10 | ≥1.0 | ≥1.3 | ≥1.6 | ≥2.0 | ≥2.4 | |
φ13 | ≥1.8 | ≥2.3 | ≥2.9 | ≥3.6 | ≥4.5 | |
φ16 | ≥2.6 | ≥3.2 | ≥4.0 | ≥5.0 | ≥6.3 | |
φ20 | ≥3.2 | ≥4.0 | ≥5.0 | ≥6.3 | ≥8.O | |
φ25 | ≥4.0 | ≥5.0 | ≥6.3 | ≥8.0 | ≥10.0 | |
φ30 | ≥4.5 | ≥5.6 | ≥7.0 | ≥9.O | ≥11.0 | |
φ38 | ≥6.0 | ≥7.5 | ≥9.3 | ≥12.0 | ≥15.0 | |
φ50 | ≥10.0 | ≥12.5 | ≥16.0 | ≥19.5 | ≥24.O | |
φ60 | ≥12.0 | ≥15.0 | ≥1.90 | ≥23.0 | ≥290 | |
φ75 | ≥15.0 | ≥19.0 | ≥23.0 | ≥29.0 | ≥37.O | |
堆积密度t/m3 | ≥1.8 | ≥1.8 | ≥1.85 | ≥1.85 | ≥1.9 |